Quote Originally Posted by PJs View Post
Beauties Doug. Quite a collection of metrics on your table there, always things to measure. Thanks for posting your new additions!

I don't recall seeing any of your posts about your heat treating systems (quench, treat, temper, etc). Is it a commercial oven or shop built? Would love to see/hear more if you are up to it.

PJ
Thanks PJs
I do my heat treating using an oxegon and accetylene torch with a 3/4" diameter rose bud tip, it gets the temp up pretty dang fast, I just go by the color of the steel, been doing it that way for many years ol pal, it's something you learn in time and through trial and error.

But I am collecting parts and pieces to build a forge, not to make knives or anything just for heat treating, these large bottles of oxegon and accetylene I have are getting real expensive to refill.

Thanks PJs
Doug